Step 7

(Dissolve the annealed product)

Drop the heat treatment vessel into a small container  and add water or add water to your heat treatment vessel if it is large enough.

Heat the water and stir until you have dissolved any of the heat treated gold/salt.

What you should have now is a nice orange liquid.

Step 8

(Dry the orange liquid)

Ok,

Same deal as step #4

Aside from drying out the liquid you may want to remove the salt by washing the end product.  I opted not to waste too much time on washing, instead I saved my wash water and claimed what would fall out over a reasonable amount of time.

My second run at this process as described here resulted in a less potent (or apparently less potent) product.

This could be some slight variation in the process between batch 1 and 2, or it could be as simple as the finer powder product in run 2 combined with the salt makes the powder sticky and less responsive to the magnetic test.

The best results I have documented are presented in the videos on Orme Research 1

  

The wash water issue boils down to this.

I have dried samples of the wash water suspecting that there are much finer particles of gold that are still floating around and I have the most interesting results.

 

It may not be obvious at first glance but these are 3 and 4 sides pyramid shapes.

Look closely and you can see that these are in fact pyramids with height and not just flat squares and triangles.

The diatomic nature of the crystals is in stark contrast to normal NaCl, table salt.

Table salt has an inverted pyramid structure that when fully grown ends up the very familiar salt crystals that are little cubes.

Apparently the gold is interlaced with the salt in such a way as to effect the crystal lattice structure.

This is what I have to share at this time as I feel it is just the beginning for greater developments in this field of endeavor.